Aluminium 3003 Sheet Plate | AMS 4008 | UNS A93003 | DIN 3.0517

ALUMINUM 3.0517 SHEETS, UNS A93003 PLATE, ASTM B209 ALUMINUM SHEETS, AISI 3003 SHEETS, ALUMINUM 3003 HOT ROLLED SHEET, ALUMINUM ALLOY 3003 COLD ROLLED SHEET, ALUMINUM 3003 SHEETS, ALUMINUM 3003 SHEET & PLATES, ALUMINUM 3003 SHEET, UNS A93003 SHEET Manufacturer in Mumbai, India.

BUY ALUMINUM 3003 CUT TO SIZE SHEETS, 3003 ALUMINUM SHEETS / PLATES STOCKIST,BUY ALUMINUM 3003 SHEETS/PLATES, ALUMINUM 3003 INDUSTRIAL SHEETS AND PLATES, ASTM B209 ALUMINUM 3003 PLATES, ALUMINUM 3003 CIRCLE Supplier in India.

3003 is the workhorse of the aluminium sheet and plate family for general fabrication. It doesn't offer the structural strength of 2014 or 7075, the marine corrosion resistance of 5083, or the heat-treatable versatility of 6061. What it does offer is a practical combination of moderate strength, excellent formability, good corrosion resistance, and reliable weldability at a cost point that makes it the logical first choice when no specific service requirement pushes the specification toward a more specialized grade.

Formability is the characteristic that most consistently positions 3003 sheet in general fabrication applications. In the H14 temper, 3003 bends, rolls, and forms with minimal springback and without surface cracking in the common range of bend radii used in production sheet metal work. In the O (annealed) temper, it deep draws well for cookware, containers, and complex formed enclosures. That combination of temper options gives fabricators flexibility to balance strength and forming severity for their specific production process.

Brazeability makes 3003 the standard specification for heat exchanger fin stock in automotive and HVAC applications. The alloy is compatible with aluminium brazing alloys and flux systems used in controlled-atmosphere and vacuum furnace brazing, which is the standard manufacturing process for aluminium radiators, air conditioning evaporators, and oil coolers. The fin material must deform during assembly of the fin-and-tube core, then survive the brazing thermal cycle without buckling or distortion. 3003's combination of formability and thermal stability through the brazing cycle makes it the established fin stock grade.

Corrosion resistance in atmospheric and general service environments is reliable and consistent. 3003 handles moisture, humidity, mild chemicals, and food-grade process environments without significant attack or surface degradation. For outdoor roofing, siding, and cladding applications where long-term appearance and surface integrity matter, 3003 performs reliably without requiring special coatings in many installation conditions.

Sheet and plate are available in H14, H24, and O tempers across a range of thicknesses and sizes with full material certification to AMS 4008 and applicable specifications including ASTM B209. Contact PM Industries for thickness, temper, width, length, and pricing.

Specification Aluminium 3003 Sheet & Plate | AMS 4008 | UNS A93003 | DIN 3.0517

Specifications	ASME SA 240/ASTM A 240
Standard Sizes	1000 x 2000 mm, 1220 x 2440 mm, 1500 x 3000 mm, 2000 x 2000 mm, 2000 x 4000 mm
Width	10-2500mm
Length	2000mm, 2440mm, 3000mm, 5800mm, 6000mm, etc
Surface	2B, 2D, BA, NO.1, NO.4, NO.8, 8K, mirror, checkered, embossed, hairline, sand, blast, Brush, etching, etc
Thickness	0.1mm to 100 mm Thk
Hardness	Quarter Hard, Half Hard,Spring Hard, Soft, Hard
Stock available in form of	Shim Sheet, Rolls, Strip, Flats, Clad Plate, Plain Sheet, Plate, Sheet, Coils, Foils, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Blank (Circle), soft annealed, sheared, annealed, tread plate,descaled, Checker Plate
Profiling	Plasma Plate Cutting
Value added services	Plasma cutting, Waterjet cutting, Laser cutting, welding, edge preparation, etc.
Test Certificates	EN 10204/3.1B, NACE MR0103, NACE MR0175
	Raw Materials Certificate
	100% Radiography Test Report
	Third Party Inspection Report, etc

Available Types of Aluminium 3003 Sheet & Plate

Aluminum 3003 Sheets & Plates – Equivalent Grades

European Standard	OLD	WNr	UNS	ISO	USA (AA)	GERMANY (DIN)
AW-AlCu4Mg1	AU4G1	3.0517	A93003	AlCu4Mg	3003	AlCuMg2

Aluminum 3003 Sheet & Plate – Chemical Composition

Al	Cr	Cu	Fe	Mg	Mn	Other Total	Si	Ti	Zn
Remainder	–	0.05 to 0.20%	0.7%	–	1.0 to 1.5%	0.15%	0.6%	–	0.10%

Aluminum 3003 Sheets & Plates – Mechanical Properties

Properties	Metric	Imperial
Tensile strength	130 MPa	18855 psi
Yield strength	125 MPa	18130 psi
Shear strength	83 MPa	12039 psi
Fatigue strength	55 MPa	7977 psi
Elastic modulus	70-80 GPa	10153-11603 ksi
Poisson’s ratio	0.33	0.33
Elongation	10%	10%
Hardness	35	35